C ≤ 0,26. Mn ≤ 1,70. Si ≤ 0,70. P ≤ 0,030. S ≤ 0,015. Cr ≤ 1,00. Ni ≤ 0,70. Mo ≤ 0,50. B ≤ 0,004.
Carbono equivalente ≤ 0,57. Rm≥ 1.400 N/mm2. ReH≥ 1.200 N/mm2. A ≥10 %. Dureza Brinell415/500Hb.
Vehicle boxes that support impacts and rust made of abrasive materials and, in general, for metallic buildings that require high elastic limit and resistance to lighten structural weigh.
Temperate, drawn stainless. Produced by water cool dawn and drawn stainless.
It can be cut by all the classic procedures (gas, plasma, water, laser).
The thickness from 4 to 10mm don’t need preheat if the oxycut operations be completed in a over temperature of 10ºC (steel temperature). On the contrary, we recommend to preheat from 100ºC to 150ºC.
Thanks to its low contain carbon chemical composition; it has a very good aptitude to soldering.
It can be weld by conventional procedures like submerged-arc welding, manual welding with electrodes or thread MIG, MAG, TIG. The energy of the welding should be controlled between 5 and 15KJ/cm.
We recommend maintaining a maximum temperature of 200ºC. It doesn’t need a preheat in thickness from 4 to 10mm.
Folded aptitude: minimum R=5x thickness in longitudinal sense.
Good aptitude to fold because of its mechanical characteristics and chemical composition with a very low contain of phosphorus and sulfur.
It’s not recommended doing it during the hot transformation given that (because) reduces the mechanical properties.
* The specifications are illustrative. For each supply we offer a certificate with the datum of the shipment delivered.
We cut your steel plates starting from your plans with absolute accuracy. An added service which allows collecting the product ready to be used.
Wide stock in steel plates with a thickness ranging from 1.5mm to 400mm and different types. Ask us for more information.
Wide range of thicknesses, from 1mm to 80mm thickness. Oxcut custom made from 8mm to more than 500mm thick