C 0,16-0,24. Mn 0,90-1,55. Si 0,20-0,50. P ≤ 0,035. S ≤ 0,025. Cr 0,80-1,20. Mo 0,15-0,50. Carbono equivalente 0,65.
Rm800/1.000 N/mm2. ReH≤ 550 N/mm2. A ≥ 14 %. Dureza Brinell 280/350 Hb. Factor antidesgaste60.
Production of pieces that require a good performance to abrasion and at the same time a good toughness. Like pots, high density blades, demolition clamps, pieces and plates for O.P equipment, etc.
It can be sold using the traditional system.
It is recommended to use dry metal flow adequate with the controlled hydrogen.
It is recommended to preheat the soldering zone, use Hilo Autrod 13-29 OK, basic Fluxocord 42/0841 TT Orlikon electrode or similar.
Warm way: should be hot forming and It is recommended to upright in the sense of lamination.
MECHANIZATION AND OXYCUT
Good. Anneal or stabilized following oxycut recommended.
|Preheating||670 - 700 ºC||Oven|
|Cementation||900 - 950 ºC||Oil, air, salts|
|Normalize||860 - 880 ºC||Air|
|Warm up||860 - 880 ºC||Oil or salts 200ºC|
|810 - 830 ºC||Oil or water|
|Drawn Stainless||150 - 200 ºC||Air|
* To mechanize easily your pieces, ask for our stabilized heat softening treatment.
* The specifications are illustrative. For each supply we offer a certificate with the datum of the shipment delivered.
We cut your steel plates starting from your plans with absolute accuracy. An added service which allows collecting the product ready to be used.
Wide stock in steel plates with a thickness ranging from 1.5mm to 400mm and different types. Ask us for more information.
Wide range of thicknesses, from 1mm to 80mm thickness. Oxcut custom made from 8mm to more than 500mm thick
Stay informed of the latest developments in the specialty steel sector before your competitors. We send you our newsletter with quality technical information.